WSD690E wholesale, Jintan, Wugang. Xifeng Wugang WSD690E, Wugang WSD690E Shaoshan, Wugang Zixing shape, WSD690E deviation, Beiliu Wugang WSD690E plate packaging, Gaomi Wugang WSD690E normalizing. WSD690E normalization in Laixi, Wugang and surface quality of Chaozhou Wugang WSD690E. Mechanical properties of WSD690E in Ruzhou, Wugang. WSD690E welding in Chenzhou, Wugang. WSD690E usage in Yulin, Wugang. WSD690E smelting method in Dali, Wugang, Zhangye, Wugang, WSD690E chemical composition. Surface quality of WSD690E in Zunyi, Wugang. Wugang Nangang health WSD690E! WSD690E quality in Yinchuan, Wugang! Wugang WSD690E steel. Test method for WSD690E of Wugang Lianjiang, Yuyao Wugang Tongren Wugang WSD690E WSD690E appearance, chemical composition, surface quality of WSD690E Wugang Qiongshan, Huaian Wugang WSD690E quality certificate, Jiaozhou Wugang Nangang WSD690E, Xinyi Wugang WSD690E Wugang WSD690E Hohhot delivery status, quality, Lanxi Wugang WSD690E ultrasonic inspection, Sihui Wugang WSD690E is what material. Zhumadian Wugang WSD690E Hubei steel, Shuangliao Wugang WSD690E delivery period, Qingyuan, Wugang WSD690E normalization,
1 scope of application:
This technical specification specifies the size of WSD690E steel plate of 8mm-50mm thickness for Volvo
Shape • allowance deviation technical requirements test method inspection rule mark and certificate of quality etc..
2 Brand
The grade is WSD690E., and the quality grade symbol is E, which represents -40C degree impact test temperature.
3 size • shape • weight and allowance deviation
The size, shape and allowable deviation of the 2006 steel plate shall be in accordance with the provisions of GB/T709 - 3.1.
The thickness deviation of the 3.2 steel plate shall be in accordance with the C class deviation in GB/T709-2006 6.1.3.
The weight of 3.3 steel plate is calculated according to theoretical weight. The thickness of the theoretical weight is the allowable thickness and the thickness of the steel plate
The arithmetic mean, the density of steel 7.85g/cm fand.
4 technical requirements
The 4.1 grade and chemical analysis (melting analysis) shall conform to the provisions of table 1.
Table 1WSD690E chemical composition of steel (melting analysis)
WT,%
Brand C Si Mn P S V Cr Ni Cu Mo B
Is less than less than or equal to less than = = = = = = =
WSD690E 0.18, 1.5, 0.02, 0.01, 0.08,, 1.5, 0.5, 0.6, 0.005, 0.5
The allowable deviation of the chemical composition of A product steel plate should comply with the provisions of GB/T2222.
B smelting carbon equivalent Ceq = 0.53%. Melting crack sensitive coefficient PCM = 0.30%.
Ceq (%) =C+Mn/6+Si/24+Ni/40+Cr/5+Mo/4+V/14
Pcm (%) =C+Si/30+Mn/20+Cu/20+Ni60+Cr/20+Mo/15+V/15+v/10+5B
4.2 smelting method
Vacuum treatment should be done immediately
4.3 delivery status
The steel plate should be quenched and tempered in the quenched and tempered heat treatment state.
4.4 mechanical properties and technological properties
The mechanical properties and technological properties of WSD690E steel sheet should be in accordance with the provisions of Table 2 in delivery.
Table 2WSD690E
The thickness of Rpo.2 Rm A V 180 degrees Charpy impact energy of cold bending test
Thickness (Mpa) (Mpa) (%) KV2 (transverse) /J d= bending center diameter
Thickness of a= sample at -40
8-50 = 680 770-940 = 14, d=3a = 47
Note A
B (V 47J steel Charpy
C according to table 2 cold bending test no crack.
4.5 ultrasonic inspection
The steel plate shall be executed at 100% JB4730.3 and shall comply with the I grade
4.6 surface quality
No bubbles on the surface of the steel plate. Scab • crack • folding • inclusion and pressed oxide scales. Steel plate shall not be layered.
The surface of the steel plate is allowed to have a thin oxide scale which does not impede the inspection of the surface defects
The surface roughness, scratch, indentation and other local defects, but its depth from the steel plate
The surface defects of steel plate can be treated by grinding, but the small thickness of the steel plate should be ensured, and the repaired parts should be smooth and without edges and corners.
Five
5.2 test method: each batch of steel plate inspection items • sampling quantity • sampling method and experimental method conform to the provisions of table 3.
5.3 steel plate with thickness greater than 40mmm, the impact test axis should be located at 1/4 of the plate thickness.
5.4 (Charpy V notch impact test results), does not comply with the provisions of article 4.4: from the same plate
3 samples were taken before and after the experiment, two groups of 6 specimens are only allowed to have 1 samples is less than the specified value, but does not allow for less than a prescribed value 70%.
5.5 the retest of other experimental items shall comply with the provisions of GB/T17505-1998
Table 3 experimental methods
Sampling number, sampling method, test method for sequence inspection items
1 Chemical Analysis of smelting 1/ GB/T2006 GB/T223 GB/T4336 per furnace
2 stretch 1/ each batch of GB/T228.1
3 cold bending 1/ GB/T2975 GB/T232 per batch
4 impact 3/ per batch of GB/T229
5 ultrasonic inspection by Zhang / JB/T4730.3
SixSurface tension / visual and measurement
7 gauges of shape and size
　
6 packing mark and certificate of quality
Packaging, marking and quality certificate of steel plate shall comply with the provisions of GB/T247-2008.
Urumqi Wugang WSD690E surface quality, nine Wugang WSD690E spot, Liaoyang Wugang WSD690E mechanical properties, high security Wugang WSD690E quality certificate, Puyang Wugang Chaohu Wugang WSD690E heat treatment, WSD690E grade, Atushi Wugang WSD690E shape, Sihui Wugang WSD690E, Jiuquan Wugang WSD690E Hulin Wugang WSD690E analysis of appearance, melting, Xinzhou Wugang WSD690E is what material Fengzhen Wugang Bayannaoer Wugang WSD690E where, WSD690E Wugang, Chongzhou WSD690E Wugang is what material. Dingxi Wugang Wugang defender WSD690E WSD690E where there is, quality certificate, Ziyang Wugang WSD690E Wugang, Lu'an WSD690E Wugang xingcheng. Ruili Wugang WSD690E implementation standards, Zibo Wugang WSD690E delivery date! Yongcheng Wugang WSD690E melting analysis, Wuchang Wugang WSD690E price, Mudanjiang Wugang WSD690E smelting method, high security Wugang WSD690E delivery status, Sanming Wugang WSD690E steel plate packaging, Longquan Wugang WSD690E shape. Longyan Wugang WSD690E where concessions, Shuangliao Wugang WSD690E delivery date, Wu Zhong Wugang WSD690E, Lengshuijiang, Wugang WSD690E surface quality.