Fengcheng high strength and toughness steel for water and electricity use WSD690E! Xiangyang Wugang WSD690E, Zoucheng high strength ductile iron and steel WSD690E where to sell, Xuchang provides WSD690E size shape, Dujiangyan supply WSD690E shock. Heilongjiang Wugang WSD690E technical requirements, Yizhou supply WSD690E. Xinle offers WSD690E! Changge hydropower steel plate WSD690E, Zhumadian hydropower steel plate WSD690E. Gaizhou high strength and toughness of WSD690E steel for Lanxi hydropower, hydropower with high strength and toughness test temperature of WSD690E steel, high strength and toughness of WSD690E steel for Jinzhou hydropower, hydropower Shishi steel WSD690E steel WSD690E, Daqing hydropower, Chuxiong WSD690E chemical experiment, high strength and toughness of WSD690E steel for Qingtongxia Hydropower, Wugang Tianchang process performance WSD690E. The lighthouse provides WSD690E delivery status. WSD690E chemical experiment supplied by lingbao,
WSD690E steel plate (the technical scheme is KTZ305-2016)
1 scope of application: this technical specification specifies the size, shape, tolerances, technical requirements, test methods, inspection rules, marks and quality certificates for WSD690E steel plates with thickness of 8mm-50mm for Volvo.
The 2 grade is WSD690E., and the quality grade symbol is E, which represents -40C degree impact test temperature.
3 size • shape • weight and allowance deviation
The size, shape and allowable deviation of the 2006 steel plate shall be in accordance with the provisions of GB/T709 - 3.1.
The thickness deviation of the 3.2 steel plate shall be in accordance with the C class deviation in GB/T709-2006 6.1.3.
The weight of 3.3 steel plate is calculated according to theoretical weight. Theoretical weight the thickness of plate thickness and allow small thickness of the arithmetic mean, the density of steel 7.85g/cm fand.
4 technical requirements
The 4.1 grade and chemical analysis (melting analysis) shall conform to the provisions of table 1. Chemical composition of 1WSD690E steel (melting analysis) wt%, grade CSiMnpsvCrNiCuMoBWSD690E is less than or equal to 0.18 = 0.5 = = 0.02 1.5 = 0.01 = 0.08 = 0.8 = 1.5 = 0.5 = 0.6 = 0.005
The allowable deviation of the chemical composition of A product steel plate should comply with the provisions of GB/T2222.
B smelting carbon equivalent Ceq = 0.53%. Melting crack sensitive coefficient PCM = 0.30%.
Ceq (%) =C+Mn/6+Si/24+Ni/40+Cr/5+Mo/4+V/14 Pcm (%) =C+Si/30+Mn/20+Cu/20+Ni60+Cr/20+Mo/15+V/15+v/10+5B
4.2 smelting method should be treated by vacuum
4.3 delivery status steel plate should be quenched and tempered quenched and tempered heat treatment delivery.
4.4 the mechanical properties and technological properties of WSD690E steel plate should comply with the provisions of Table 2 in the delivery state of mechanical properties and technological properties. Table 2WSD690E Rpo.2 Rm A V thickness of Charpy impact energy of 180 DEG bending experimental thickness (Mpa) (Mpa) (%) KV2 (horizontal) /J d= bend diameter thickness -40 C a= sample thickness 8-50 = 680 770-940 = 14, d=3a = 47
A (V 47J C B steel Charpy according to table 2 there shall be no crack of cold bending test.
4.5 ultrasonic inspection steel plate should be followed by 100% JB4730.3, should comply with I class
4.6 surface quality steel plate shall not contain bubbles • scab • crack • folding • inclusion and pressed oxide scales. Steel plate shall not be layered. The steel surface allows - - Scratch indentation and other local defects of thin iron oxide rust - - does not interfere with the inspection of surface defects caused by pressing iron oxide off the rough surface, but the depth from the surface defects of steel plate steel plate allows real grinding processing, but should ensure that the small thickness, repair should be smooth without edges. 55.2 test method: each batch of steel plate inspection items • sampling quantity • sampling method and experimental method conform to the provisions of table 3.
5.3 steel plate with thickness greater than 40mmm, the impact test axis should be located at 1/4 of the plate thickness.
5.4 (Charpy V notch impact test results), does not comply with the provisions of article 4.4 of the 3 samples from the same plate and then carries on the experiment, the two groups before and after the 6 samples are only allowed to have 1 samples is less than the specified value, but does not allow for less than a prescribed value 70%.
The number of sampling test method shall comply with the provisions of GB/T17505-1998 Table 3 experimental method of inspection item sampling 1 smelting chemical analysis 1/ GB/T2006 GB/T223 of each furnace tank number GB/T4336 2 GB/T228.1 3 1/ tensile each batch of each batch of GB/T2975 GB/T232 4 1/ cold shock 3/ of each batch of GB/T229 5 / JB/T4730.3 6 by ultrasonic inspection and measurement by surface / visual 7 dimensional shape by measuring / appropriate retesting 5.5 other experimental items
6 packing / marking and quality certificate steel plate packaging and marking and quality certificate should comply with the provisions of GB/T247-2008.
Hainan high strength and toughness steel WSD690E factory, Kaifeng Wugang WSD690E. WSD690E test temperature in Changzhi, Wugang, Ali provides WSD690E, Shijiazhuang Wugang WSD690E smelting method, high strength and toughness of hydropower steel WSD690E. Heilongjiang Wugang WSD690E technical requirements, Yumen high strength and toughness steel for hydropower use WSD690E, Meishan Wugang WSD690E ultrasonic flaw detection, Longjing supply WSD690E technical requirements, Xuchang provide WSD690E size shape, Rugao Wugang WSD690E technical requirements! Supply WSD690E smelting method, Heyuan Wugang WSD690E delivery status. Size profile of Wugang WSD690E. Xinghua provides WSD690E, Fengcheng provides WSD690E chemical experiment, Hanchuan provides WSD690E test temperature, Xuchang provides WSD690E size profile, Qinghai supply WSD690E delivery status,