Xinyu hydropower steel WSD690E stretching, Wugang WSD690E, Pizhou WSD690E, Wugang WSD690E supply for Ning, WSD690E size. Yangzhong high strength and toughness hydropower steel WSD690E technical requirements, Huludao hydropower steel WSD690E which sell, Chengdu provides WSD690E which sell, Beiliu provides WSD690E, high strength and toughness steel WSD690E price, Dali Wugang WSD690E, Qingyang hydropower steel plate WSD690E impact. Wugang WSD690E, Shantou Wugang WSD690E Wugang WSD690E Fuqing, which has sold Lianzhou Wugang WSD690E, high strength and toughness of WSD690E steel for Wanyuan hydropower, hydropower in Yancheng steel WSD690E size, Shantou WSD690E Wugang, Qiongshan WSD690E.
WSD690E steel plate (the technical scheme is KTZ305-2016)
1 scope of application: this technical specification specifies the size, shape, tolerances, technical requirements, test methods, inspection rules, marks and quality certificates for WSD690E steel plates with thickness of 8mm-50mm for Volvo.
The 2 grade is WSD690E., and the quality grade symbol is E, which represents -40C degree impact test temperature.
3 size • shape • weight and allowance deviation
The size, shape and allowable deviation of the 2006 steel plate shall be in accordance with the provisions of GB/T709 - 3.1.
The thickness deviation of the 3.2 steel plate shall be in accordance with the C class deviation in GB/T709-2006 6.1.3.
The weight of 3.3 steel plate is calculated according to theoretical weight. Theoretical weight the thickness of plate thickness and allow small thickness of the arithmetic mean, the density of steel 7.85g/cm fand.
4 technical requirements
The 4.1 grade and chemical analysis (melting analysis) shall conform to the provisions of table 1. Chemical composition of 1WSD690E steel (melting analysis) wt%, grade CSiMnpsvCrNiCuMoBWSD690E is less than or equal to 0.18 = 0.5 = = 0.02 1.5 = 0.01 = 0.08 = 0.8 = 1.5 = 0.5 = 0.6 = 0.005
The allowable deviation of the chemical composition of A product steel plate should comply with the provisions of GB/T2222.
B smelting carbon equivalent Ceq = 0.53%. Melting crack sensitive coefficient PCM = 0.30%.
Ceq (%) =C+Mn/6+Si/24+Ni/40+Cr/5+Mo/4+V/14 Pcm (%) =C+Si/30+Mn/20+Cu/20+Ni60+Cr/20+Mo/15+V/15+v/10+5B
4.2 smelting method should be treated by vacuum
4.3 delivery status steel plate should be quenched and tempered quenched and tempered heat treatment delivery.
4.4 the mechanical properties and technological properties of WSD690E steel plate should comply with the provisions of Table 2 in the delivery state of mechanical properties and technological properties. Table 2WSD690E Rpo.2 Rm A V thickness of Charpy impact energy of 180 DEG bending experimental thickness (Mpa) (Mpa) (%) KV2 (horizontal) /J d= bend diameter thickness -40 C a= sample thickness 8-50 = 680 770-940 = 14, d=3a = 47
A (V 47J C B steel Charpy according to table 2 there shall be no crack of cold bending test.
4.5 ultrasonic inspection steel plate should be followed by 100% JB4730.3, should comply with I class
4.6 surface quality steel plate shall not contain bubbles • scab • crack • folding • inclusion and pressed oxide scales. Steel plate shall not be layered. The steel surface allows - - Scratch indentation and other local defects of thin iron oxide rust - - does not interfere with the inspection of surface defects caused by pressing iron oxide off the rough surface, but the depth from the surface defects of steel plate steel plate allows real grinding processing, but should ensure that the small thickness, repair should be smooth without edges. 55.2 test method: each batch of steel plate inspection items • sampling quantity • sampling method and experimental method conform to the provisions of table 3.
5.3 steel plate with thickness greater than 40mmm, the impact test axis should be located at 1/4 of the plate thickness.
5.4 (Charpy V notch impact test results), does not comply with the provisions of article 4.4 of the 3 samples from the same plate and then carries on the experiment, the two groups before and after the 6 samples are only allowed to have 1 samples is less than the specified value, but does not allow for less than a prescribed value 70%.
The number of sampling test method shall comply with the provisions of GB/T17505-1998 Table 3 experimental method of inspection item sampling 1 smelting chemical analysis 1/ GB/T2006 GB/T223 of each furnace tank number GB/T4336 2 GB/T228.1 3 1/ tensile each batch of each batch of GB/T2975 GB/T232 4 1/ cold shock 3/ of each batch of GB/T229 5 / JB/T4730.3 6 by ultrasonic inspection and measurement by surface / visual 7 dimensional shape by measuring / appropriate retesting 5.5 other experimental items
6 packing / marking and quality certificate steel plate packaging and marking and quality certificate should comply with the provisions of GB/T247-2008.
Chishui hydropower steel WSD690E, high strength and toughness of WSD690E steel for Foshan hydropower steel manufacturers, WSD690E manufacturers in Daye Hydropower hydropower, steel WSD690E, Lu'an WSD690E, Shaoxing WSD690E, Ruichang hydropower with high strength and toughness test temperature of steel WSD690E used for steel plate, Ji'nan hydropower WSD690E, Heilongjiang Wugang WSD690E, Huaying WSD690E, Botou Wugang WSD690E, Dali Wugang WSD690E, Zhangye Wugang WSD690E smelting method, Heilongjiang Wugang WSD690E technical requirements, Liyang Wugang WSD690E, Qinghai supply WSD690E delivery status. Dujiangyan supply WSD690E impact, Zhaotong Wugang WSD690E technical requirements, Dongying hydropower steel plate WSD690E ultrasonic flaw detection, supply WSD690E smelting method,