Company name: Wuyang iron and Steel Co., Ltd.
Contact: Chen Jie
Cell phone number: 15617588651
Impact of WSD690E on steel plate for Hetian hydropower station, applicable range of Laixi hydropower steel plate WSD690E. Pulandian hydropower steel plate WSD690E, Chongzuo provides WSD690E process performance. Qingtongxia Hydropower high strength and high toughness steel WSD690E. The rock provides WSD690E. Xingcheng offers WSD690E. Test temperature of WSD690E for high strength and toughness hydropower steel in Lanxi. Provide WSD690E manufacturers! Baise provides WSD690E chemical experiment, Zhuhai hydropower steel plate WSD690E size shape, Tongzhou supply WSD690E, Xinmin steel plate WSD690E test temperature, Daqing hydropower steel plate WSD690E. Test temperature of WSD690E for high strength and toughness hydropower steel in Ruichang. Hubei hydropower steel WSD690E manufacturers, high strength and toughness of WSD690E steel for Shangzhi hydropower. Jingzhou provides WSD690E, Wendeng provides WSD690E, and Anqiu provides WSD690E.
WSD690E plate (process execution of the technical conditions for the KTZ305-2016) 1 Scope: this specification provides for Volvo steel plate with a thickness of WSD690E 8mm-50mm - shape - size allowable deviation - technical requirements, test methods, inspection rules and quality certificates and other marks. The 2 grade is WSD690E., and the quality grade symbol is E, which represents -40C degree impact test temperature. 3 size • shape • weight and allowable deviation 3.1 steel plate size • shape and allowable deviation should comply with the provisions of GB/T709 - 2006. The thickness deviation of the 3.2 steel plate shall be in accordance with the C class deviation in GB/T709-2006 6.1.3. The weight of 3.3 steel plate is calculated according to theoretical weight. Theoretical weight the thickness of plate thickness and allow small thickness of the arithmetic mean, the density of steel 7.85g/cm fand.4 technology 4.1 grade and chemical form (melting analysis) should meet the specification in table 1. Chemical composition of 1WSD690E steel (melting analysis) wt%, provisions of chemical composition CSiMnpsvCrNiCuMoBWSD690E = 0.18 = 0.5 = 1.5 = 0.02 = 0.01 = 0.08 = 0.8 = 1.5 = 0.5 = 0.6 = 0.005A finished steel plate should be consistent with the allowable deviation of GB/T2222. B smelting carbon equivalent Ceq = 0.53%. Melting crack sensitive coefficient PCM = 0.30%. Ceq (%) =C+Mn/6+Si/24+Ni/40+Cr/5+Mo/4+V/14 Pcm (%) =C+Si/30+Mn/20+Cu/20+Ni60+Cr/20+Mo/15+V/15+v/10+5B 4.2 should be handled by the vacuum smelting method just 4.3 delivery state plates should be state delivery to heat quenching and tempering treatment. 4.4 the mechanical properties and technological properties of WSD690E steel plate should comply with the provisions of Table 2 in the delivery state of mechanical properties and technological properties. Table 2WSD690E Rpo.2 Rm A V thickness of Charpy impact energy of 180 DEG bending experimental thickness (Mpa) (Mpa) (%) KV2 (horizontal) /J d= bend diameter thickness -40 C a= specimen thickness 8-50 = 680, 770-940 = 14 = 47 d=3a A B V 47J C (Charpy plate cold bending test according to table 2 there shall be no crack. 4.5 ultrasonic inspection steel plate should be followed by 100% JB4730.3, should comply with I class 4.6 surface quality, steel plate surface shall not have bubble, crack, crack, folding, inclusion and pressing into the oxide scale. Steel plate shall not be layered. The steel surface allows - - Scratch indentation and other local defects of thin iron oxide rust - - does not interfere with the inspection of surface defects caused by pressing iron oxide off the rough surface, but the depth from the surface defects of steel plate steel plate allows real grinding processing, but should ensure that the small thickness, repair should be smooth without edges. 55.2 test method: each batch of steel plate inspection items • sampling quantity • sampling method and experimental method conform to the provisions of table 3. 5.3 steel plate with thickness greater than 40mmm, the impact test axis should be located at 1/4 of the plate thickness. 5.4 (Charpy V notch impact test results), does not comply with the provisions of article 4.4 of the 3 samples from the same plate and then carries on the experiment, the two groups before and after the 6 samples are only allowed to have 1 samples is less than the specified value, but does not allow for less than a prescribed value 70%. 5.5 other experimental projects of reinspection shall be packed, mark and quality certificate number method according to sampling method test GB/T17505-1998 the provisions of Table 3 experimental methods 1 sampling inspection project smelting chemical analysis 1/ GB/T2006 GB/T223 of each furnace tank number GB/T4336 2 GB/T228.1 3 1/ tensile each batch of each batch of GB/T2975 GB/T232 4 1/ cold shock 3/ of each batch of GB/T229 5 ultrasonic flaw detection by one by one surface 6 / JB/T4730.3 / visual and measuring 7 dimensions shape one by one / the right tools - 6 packaging marking and certification plate should be consistent with GB/T247-2008.
Liyang Wugang WSD690E, Aletai hydropower steel plate WSD690E, Shuangliao supply WSD690E tensile, provide WSD690E mechanical properties, silver high strength toughness steel WSD690E, Suzhou Wugang WSD690E mechanical properties, Fuding provide WSD690E. WSD690E delivery status, high strength and toughness of hydropower steel WSD690E! WSD690E ultrasonic flaw detection in Hebei, Wugang. Guangyuan hydropower steel plate WSD690E, Dongtai Wugang WSD690E smelting method, Linfen high strength and toughness hydropower steel WSD690E, Leizhou provides WSD690E process performance, Ji'nan hydropower steel plate WSD690E applicable range, Shanghai high strength and toughness steel WSD690E. Wuhan iron and steel WSD690E where to sell, Yinchuan supply WSD690E. Suqian supplies WSD690E. Huaihua hydropower steel plate WSD690E,