Company name: Wuyang iron and Steel Co., Ltd.
Contact: Chen Jie
Cell phone number: 15617588651
Binzhou XG08 plate used in the production of where to buy, how much money the Ruichang XG08 zinc pot, Jujube XG08 steel manufacturers sell Shiyan XG08 steel prices, Haixi, Linzhou XG08 production by money, Xinyang steel, Xianyang XG08 zinc pot long-term sales, where the Heshan XG08 steel to buy, sell Wuzhou XG08 galvanized steel. Nantong XG08 galvanized steel for a long time supply, Yinchuan XG08 steel supply, the Lengshuijiang XG08 steel manufacturers supply. Xiangtan XG08 steel where to buy, Xiaoyi XG08 zinc pan steel plate supply, Changge XG08 production steel plate manufacturers supply. Fuzhou XG08 production steel sales point. Chaohu XG08 steel zinc pot. Zhongxiang, Tacheng XG08 zinc pot for a long time supply!
XG08 zinc pot production steel plate 1. brand "XG08", "WKS", "WDT0b" and German imported steel materials, mainly used for storage of zinc liquid needed. Zinc content of zinc pot is 200 tons. By controlling the composition of zinc liquid, the product has high appearance quality, mechanical processing property and some defects caused by improper control of zinc liquid composition. Rimmed steel is an incomplete deoxidizing steel. When pouring, the molten steel is boiling in the ingot mold (gas escaping), and the amount of silicon in the steel is very low. C, Si, Mn, P, S content of 2. chemical composition characteristics of the material is low, such as C < 0.08, Si < 0.03, can effectively resist the corrosion of zinc. The current hot-dip galvanizing cooker in China is usually welded with high quality low carbon steel plates such as 08F or 05F. However, due to the strong corrosion of molten zinc to steel materials, the service life of the container is very short. Generally speaking, the service life of domestic hot-dip galvanizing pan is 3 months to 2 years. 3.XG08 C Cr Mn steel chemical composition elements P Si Cu Ni in < 0.08 = 0.10 0.25-0.50 = 0.035 = 0.03 = 0.20 = 0.30 4.XG08 mechanical properties experimental yield strength tensile strength elongation contraction of each element is greater than or equal to 295MPa rate of hardness value is larger than 175MPa 35% 60% 131HB 5. steel in zinc plating of carbon: 1): the carbon content is high iron zinc diffusion reaction more intense, the greater the loss of iron loss, deterioration of alloy layer thickening adhesion. Low carbon steel in general use of 0.05~0.15. 2) silicon: high silicon content will increase the thickness of the alloy layer and form a gray coating to influence the adhesion. Rimmed steel and aluminum steel with a silicon content of less than 0.07% are used as galvanized substrates. 3) copper: Copper in steel base can slow down the pickling speed, but it has no bad effect on hot dip galvanizing, and at the same time, it can improve corrosion resistance. When manufacturing special purpose corrosion resistant galvanized sheet, it often chooses steel grade of 0.2~0.3%. 4) titanium: steel containing 0.2% titanium plays an important role in zinc plating. Titanium is the main addition element to produce low alloy and high strength galvanized steel. It plays an important role in the steel in the presence of TiC and TiN. 5) the content of manganese, sulfur, phosphorus and sulfur has little influence on the structure of zinc layer, but the content of phosphorus is about 0.15%, the zinc layer has no luster spots and the adhesion is bad. 6) aluminum: aluminum is the main additive in zinc solution, generally 0.15~0.22%, aluminum has an important effect on zinc plating: A and aluminum content reach 0.03%, which can increase zinc sheen. B and aluminum can produce an extremely thin intermediate layer of five aluminized two iron, which can inhibit the growth of the iron zinc alloy layer and increase the adhesion of the zinc layer. C and aluminum can affect the viscosity of zinc liquid and make the zinc layer thicker or thinner. D and aluminum can reduce the number of copper resistance tests. E, too much aluminum can reduce the solubility of iron in the zinc liquid, generate more zinc. 7) iron: harmful elements can increase the viscosity of the liquid zinc, the zinc layer thickness, formation of slag. The general control is below 0.05%. 8) cadmium: 0.1~0.5% can increase the zinc flower. After 0.5%, the alloy layer can be thickened and the toughness is reduced. General control is less than 0.03%. 9) lead: beneficial element, can improve the wettability of zinc liquid and increase zinc flower. Lead generally controls 0.06~0.08% when galvanizing with lead containing hot-dip galvanizing method.
Yiyang XG08 galvanized steel cutting, Qingdao XG08 galvanized steel manufacturers, Honghu, Gaizhou XG08 zinc pot sales point, Jiaxing XG08 agent, Tianjin XG08 galvanized steel office. Macheng XG08 steel plate manufacturing. Chongzuo XG08 production steel distributor, Taishan XG08 zinc pot where to buy, Beiliu XG08 steel factory, cooperation XG08 zinc pot how much, Yulin, Baoshan XG08 steel how much, Laiwu XG08 galvanized steel wholesalers, Xuzhou XG08 steel processing, Miquan XG08 zinc pot spot. Cangzhou XG08 supply, Xuzhou, Ganzhou XG08 zinc Pan Steel Plate dealer, guest XG08 zinc pan steel plate.