American Standard brands: GR1, GR2, GR3, GR5, GR7, GR12
Russian plate number: BT1-00, BT1-0, BT1-2, etc.
Domestic brands: TA0, TA2, TA3, TA5, TA6, TA7, TA9, TA10, TB2, TC1, TC2, TC3,, TC4,
A reference standard
GB 1: 228 metal tensile test method
Grade and chemical composition of GB/T 2: 3620.1 titanium and titanium alloy
Chemical composition and composition tolerance of GB/T3620.2 3: titanium and titanium alloy products
Methods for chemical analysis of GB 4: 4698 sponge titanium, titanium and iron alloys
Titanium plate specifications
Grade TA1, TA2, TA3, TC4, GR1, GR2, GR5,
Standard 3621-2007 GB/T, 13810-2007ASTM B265 GB/T, F136 ASTM, F67 ASTM,
Size 0.5-5.0mm x W1000mm T x L 2000-3500mmT 6.0- 30mm x W1000-2500mm x L 3000-6000mmT 30- 80mm x W1000mm x L 2000mm
Use of metallurgy, electronics, medical, chemical, petroleum, pharmaceutical, aerospace, etc..
Deviation of titanium plate thickness
Thickness (mm) thickness tolerance (mm)
(3.71 to 4.76), excl 0.36
3.33 to 0.31 3.68
2.92 to 0.25 3.30
2.51 to 0.23 2.90
2.13 to 0.20 2.49
1.85 to 0.18 2.11
1.50 to 0.15 1.83
1.04 to 0.13 1.47
0.69 to 0.10 1.02
0.43 to 0.08 0.66
0.20 to 0.05 0.41
0.15 to 0.04 0.18
0.03 0.13
Hot working state (R)
Cold working condition (Y)
Annealing state (M)
Titanium plate manufacturing process editor
Forging process for hot forging above metal recrystallization temperature.
The rolling process of hot rolling at a higher temperature than the recrystallization temperature.
The rolling process of the cold rolling plastic deformation temperature is lower than the recovery temperature.
Annealing: the metal is slowly heated to a certain temperature, to maintain sufficient time, and then to the appropriate speed of cooling (usually slow cooling, and sometimes control cooling) of a metal heat treatment process.
Pickling: the workpiece is immersed in sulfuric acid and other aqueous solution to remove the metal surface of the oxide film. Is a pre-treatment or intermediate treatment of electroplating, enamel, rolling and other processes [1]
Features of titanium plate
1 kinds of titanium oxide film on the surface of the plate is equivalent to a good durability with separating agent, using titanium plate saves separating agent, so the plate is easy to peel, eliminates the process of plate pretreatment, titanium plate is lighter than copper in half.
2 titanium plate life is more than 3 times of the copper plate, according to the operating conditions of up to 20 to 10 years
3 the electrolytic copper produced by the titanium board is compact, and the surface is smooth and the quality is excellent.
4 as a result of the titanium board does not need to apply the separation agent, thus can avoid the pollution of copper electrolyte.
5 increase production capacity to reduce the production cost of electrolytic copper, and thus have better economic benefits